Copper Alloy C11000

General Characteristics
C11000 is Electrolytic tough pitch copper C11000 is made from cathode copper, that is, copper that has been refined electrolytically. C11000 is the most common of all the electrical coppers. It has high electrical conductivity, in excess of 100% IACS.

Produced in all forms except pipe and used for building fronts, down-spouts, flashing, gutters, roofing, screening, spouting, gaskets, radiators, busbars, electrical wire, stranded conductors, contacts, radio parts, switches, terminals, ball floats, butts, cotter pins, nails, rivets, soldering copper, tacks, chemical process equipment, kettles, pans, printing rolls, rotating bands, roadbed expansion plates.
Typical Chemical Composition

Weight % Cu + Ag O

minimum — —

maximum 99.9 0.04

Weight %	Cu + Ag	O
minimum	—	—
maximum	99.9	0.04

Characteristics			English	Metric
Nominal density (68°F/20°C)			0.323 lbs/in³	8.94 g/cm³
Melting range			1949 – 1981 °F	1065 – 1083 °C
Specific heat (212 °F/100°C)			0.092 BTU/lb – °F	385 J/KG- °K
Coefficient of thermal expansion	68°F – 212°F 20°C – 100°C		9.4 micro in/in- °F	17.0 micro m/m- °K
	68°F – 392°F 20°C – 200°C		9.6 micro in/in- °F	17.3 micro m/m- °K
	68°F – 572°F 20°C – 300°C		9.8 micro in/in- °F	17.7 micro m/m- °K
Thermal conductivity	20°C / 68°F		224 BTU/ft- hr – °F	388 W/m – °K
	100°C / 212°F		220 BTU/ft- hr – °F	380 W/m – °K
	300°C / 572°F		214 BTU/ft- hr – °F	370 W/m – °K
Electrical resistivity	O60	-100-200°C	17.00 – 17.24 nΩ · m
Electrical resistivity	H14	0-100°C	1.78 nΩ · m

Temper		Tensile					Hardness	Shear
		Ultimate		Yield		Elongation in 50 mm (2 in.)	Rockwell F	Shear strength
		KSI	MPa	KSI	MPa	%		KSI	MPa
OSO25 – Average grain size 0.025 mm	25 mm (1 in.) outside diameter, 1.65 mm (0.065 in.) wall thickness	34	235	11	76	45	45	23	160
OSO50 – Average grain size 0.050 mm		32	220	10	69	45	40	22	150
H55 – Light drawn, light cold rolled (15% C.W.)		40	275	220	32	25	77	26	180
H80 – Hard drawn (40% C.W.)		55	380	50	345	8	95	29	200

Copper Alloy C11000 Sales:+972 4 618 2000

General Characteristics
C11000 is Electrolytic tough pitch copper C11000 is made from cathode copper, that is, copper that has been refined electrolytically. C11000 is the most common of all the electrical coppers. It has high electrical conductivity, in excess of 100% IACS.

Produced in all forms except pipe and used for building fronts, down-spouts, flashing, gutters, roofing, screening, spouting, gaskets, radiators, busbars, electrical wire, stranded conductors, contacts, radio parts, switches, terminals, ball floats, butts, cotter pins, nails, rivets, soldering copper, tacks, chemical process equipment, kettles, pans, printing rolls, rotating bands, roadbed expansion plates.
Typical Chemical Composition

Weight % Cu + Ag O

minimum — —

maximum 99.9 0.04

Weight %	Cu + Ag	O
minimum	—	—
maximum	99.9	0.04

Characteristics			English	Metric
Nominal density (68°F/20°C)			0.323 lbs/in³	8.94 g/cm³
Melting range			1949 – 1981 °F	1065 – 1083 °C
Specific heat (212 °F/100°C)			0.092 BTU/lb – °F	385 J/KG- °K
Coefficient of thermal expansion	68°F – 212°F 20°C – 100°C		9.4 micro in/in- °F	17.0 micro m/m- °K
	68°F – 392°F 20°C – 200°C		9.6 micro in/in- °F	17.3 micro m/m- °K
	68°F – 572°F 20°C – 300°C		9.8 micro in/in- °F	17.7 micro m/m- °K
Thermal conductivity	20°C / 68°F		224 BTU/ft- hr – °F	388 W/m – °K
	100°C / 212°F		220 BTU/ft- hr – °F	380 W/m – °K
	300°C / 572°F		214 BTU/ft- hr – °F	370 W/m – °K
Electrical resistivity	O60	-100-200°C	17.00 – 17.24 nΩ · m
Electrical resistivity	H14	0-100°C	1.78 nΩ · m

Temper		Tensile					Hardness	Shear
		Ultimate		Yield		Elongation in 50 mm (2 in.)	Rockwell F	Shear strength
		KSI	MPa	KSI	MPa	%		KSI	MPa
OSO25 – Average grain size 0.025 mm	25 mm (1 in.) outside diameter, 1.65 mm (0.065 in.) wall thickness	34	235	11	76	45	45	23	160
OSO50 – Average grain size 0.050 mm		32	220	10	69	45	40	22	150
H55 – Light drawn, light cold rolled (15% C.W.)		40	275	220	32	25	77	26	180
H80 – Hard drawn (40% C.W.)		55	380	50	345	8	95	29	200